Tempering Glass Heat Soak Furnace

Glass Tempering Furnace is for tempering glass. Tempered glass could have spontaneous breakage without receiving any external force, which is the nature of tempered glass. The reason comes from nickel sulfide inside the glass. Nickel sulfide is a~Nis in high temperature during the heating section of tempering procedure. When cooled rapidly in cooling section, there is no enough time for it to turn β -Nis of low temperature. The morphic transformation will last for ten of years after the tempering glass is installed. Leading to spontaneous breakage. Heat soak furnace is assistant equipment to tempering. Upon completion of glass tempering procedure, to avoid breakage happens after installation. This increase the safety and reliability of building. The machine is characteristic of computer in-process monitoring and controlling, multi curve display, data storage, record check and curve printing, The machine can be extended to be used in drying low frit heating and pre-pressing of bending lamination in glass. The machine can be customized.NO. Item L(mm) W(mm) H(mm) 1 Dimension of furnace 7200 2280 2200 2 Dimension of rack 4800 2060 1190 3 Dimension of loading table 2600 2300 1610 4 Occupied area 15000 2300 - 5 Installed power 68KW-130KW 6 Cycle of heating 50-90 mins /furnace(4+0.38+4) 7 Working temperature 85-300 centigrade 8 Vacuuming -0.1MPa